PVC FOAM |
|
CELLFOAM ® Is a lightweight, PVC closed cell foam for universal use in sandwich constructions. Its excellent stiffness and strength to weight ratio and high toughness make it suitable for a large variety of applications. The foam is ideally suited for statically and dynamically loaded structures and is compatible to all resin systems. It has the following main characteristics: · High strength and stiffness to weight ratio · Rot resistant · Good thermal insulation · Self extinguishing, good fire behaviour · Very low water absorption
More information about PVC foam core. |
|
Copyright 2007 © FIBERMAX COMPOSITES |
|
View price of PVC Foam core on new Fibermax Composites website. |
|
|
TYPES |
||||||
|
|
M 30 |
M 40 |
M 55 |
M 75 |
M 90 |
M 130 |
M200 |
|
NOMINAL DENSITY ISO 845 KG/M3 |
33 |
40 |
60 |
80 |
100 |
130 |
200 |
|
THERMAL CONDUCTIVITY COEFF. ISO 830 |
0.022 |
0.031 |
0.031 |
0.033 |
0.035 |
0.039 |
0.048 |
|
THERMAL BENDING STABILITY DIN 53424 oC |
80 |
80 |
85 |
85 |
90 |
95 |
100 |
|
MINIMUM TEMPERATURE TESTED oC |
-200 |
-200 |
-200 |
-200 |
-200 |
-200 |
-200 |
|
FIRE RESISTING PROPERTY ASTM D 1692-67T |
M2 |
M2 |
M2 |
M2 |
M2 |
M2 |
M2 |
|
THERMAL EXPANSION COEFF X10-6Co |
40 |
40 |
40 |
35 |
35 |
30 |
25 |
|
COMPRESIVE MODULUS DIN 53421 N/mm2 |
21 |
34 |
58 |
83 |
110 |
155 |
260 |
|
COMPRESIVE STRENGTH ISO 844 N/mm2 |
0.3 |
0.45 |
0.85 |
1.30 |
1.90 |
2.60 |
4.80 |
|
TENSILE MODULUS DIN 53437 N/mm2 |
18 |
28 |
45 |
63 |
81 |
115 |
180 |
|
TENSILE STRENGTH DIN 53571 N/mm2 |
0.60 |
0.70 |
1.30 |
2.00 |
2.70 |
3.80 |
6.20 |
|
SHEAR MODULUS ASTM C393 N/mm2 |
|
13 |
22 |
30 |
38 |
50 |
75 |
|
SHEAR STRENGTH ISO 1922 N/mm2 |
|
0.45 |
0.80 |
1.20 |
1.60 |
2.30 |
3.50 |
|
FLECTUAL MODULUS ISO 1209 N/mm2 |
13 |
24 |
40 |
70 |
80 |
120 |
160 |
|
BENDING STRENGTH DIN 53423 N/mm2 |
0.4 |
0.6 |
1.4 |
2.1 |
2.5 |
3.0 |
3.5 |